Offer Novolac Epoxy Vinyl Ester Resins From China

Model No.: SWANCOR 907

CAS No.: un-available

Other Names: VE resin

MF: un-available

EINECS No.: un-available

Type: Synthetic Resin And Plastics

Brand Name: Swancor

Model Number: 901-200

Appearance: Light yellow transparent liquid

Density: 1.06±0.02kg/L

Viscosity: 430±150 cps (LVT#3-60rpm/25℃)

solid content: 62±1.5%

Gel time: 15-25min

storage period: 4 month(below 25℃)

Manufacturing process: filament winding or spray up process

feature: high distortion temperature

Application: high-temperature flue and smoke pipe

Delivery Time: 20 days after deposit in account

Place of Origin: Jiangsu, China

Purity: 55%

SWANCOR 907 Novolac Epoxy Vinyl Ester Resins

SWANCOR 907 series products are phenolic epoxy vinyl ester resins with high crosslinking density and good heat resistance (The heat distortion temperature can reach 150 ℃ or even higher), especially for chlorine-containing solutions or organic solvents. It can be used in some occasions where the temperature is relatively high, such as the preparation of high-temperature flue and smoke pipe, and in the chlor-alkali industry, papermaking Industry, oil and gas storage, electroplating industry, metal smelting industry, etc. are also widely used.

1. Surperior mechanical properties and chemical resistance at elevated temperature.

2. High heat distortion temperature

3. With excellent fatique resistance.

4. Suitable for more aggressive corrossive applications.

5. Lower casting color

Novolac Epoxy Vinyl Ester Resins

Novolac Epoxy Vinyl Ester Resins Product appearance

Polyester resin casting body property

Appearance	light yellow transparent liquid
Density	1.06±0.02kg/L
Viscosity	430±150 cps (LVT#3-60rpm/25℃)
Solid content	62±1.5%
Gel time	15-25min (55%MEKPO：1.2%，6% cobalt Octoate 0.4%，100%DMA：0.05%，temperature：25℃ water bath)
Storage period	4 month(below 25℃)

Product data sheet

Item	Data	Test method
Tensile strength	76-90MPa	ASTM D 638
Tensile modulus	3.4-3.7GPa	ASTM D 638
Elongation	2.5-4.0%	ASTM D 638
Bending strength	124-145MPa	ASTM D 790
Bending modulus	3.7-4.1GPa	ASTM D 638
Distortion temperature	144-150℃	ASTM D 638
Hardness	40-46 Barcol	ASTM D 2583