Model No.: TC-907
CAS No.: 25608-12-2
Other Names: Novolac type epoxy vinyl ester resin
MF: C3H5NO)n
EINECS No.: 208-750-2
Type: Synthetic Resin And Plastics
Brand Name: thousands chemicals
Model Number: 907, 907
Appearance: Transparent clear yellow liquid
Density: 1.06±0.02
Viscosity: 270-400cps(LVT#3-60rpm/25℃)
solid content: 67 %
Gel time: 15-25min
storage period: 4 month(below 25°C)
packed in: metal barrel
Package: 220kg/barrel 85.6us gallon/barrel
Keywords: vinyl ester resin
Place of Origin: Jiangsu, China
Purity: 66-72
Packaging: metal barrel
Supply Ability: 1000000000 Ton/Tons per Year
Port: Shanghai Port
TC-907 is Novolac epoxy vinyl ester resin. It combines excellent mechanical properties at high temperatures, such as tensile strength, bending strength, excellent chemical mixtures, oxidizing chemicals and solvents for corrosion. TC-907 is widely used for its excellent toughness and fatigue resistance due to its special properties at high temperatures.
w Chemical storage tanks, pipes, flue gas desulfurization systems (FGD), scrubbers, ducts.
w Corrosion resistant flooring while incorporated with aggregates.
w Equipment specified to handle mixture of air, exhaust gases or potentially flammable liquids.
w Can be easily applied by hand lay-up laminating, spray-up, pultrusion, resin transfer molding (RTM) and filament winding.
w Can be used in polymer concrete casting.
w Can comply with US FDA regulation 21 CFR 177.2420 if the resin is properly formulated and cured.
|
Appearance |
Clear amber liquid |
|
|
Solid Content (%) |
68 ± 2 |
|
|
Viscosity *1 |
335 ± 65cps |
335 ± 65 mPa.s |
|
Specific Gravity |
1.06 ± 0.02 |
|
|
Gel Time (min)*2 |
20 ~ 30 |
|
|
Shelf Life (months) |
6(25oC) |
|
*1 LVT-#3-60rpm@25oC.
*2 6%Cobalt: 0.4phr, 100% DMA: 0.05phr, 80%CHP: 1.2phr @25oC.
|
Property |
SI |
US Standard |
Test Method |
|
Tensile Strength |
76~90MPa |
11,000~13,000psi |
ASTM D638 |
|
Tensile Modulus |
3.5~3.7GPa |
5.0~5.3 X105 psi |
ASTM D638 |
|
Tensile Elongation |
2.0~4.0% |
2.0~4.0% |
ASTM D638 |
|
Flexural Strength |
124~145MPa |
18,000~21,000psi |
ASTM D790 |
|
Flexural Modulus |
3.6~4.1GPa |
5.2~5.9 X105 psi |
ASTM D790 |
|
Volume Shrinkage |
8.5~9.5% |
8.5~9.5% |
ASTM D2566 |
|
Heat Distortion Temperature*4 |
144~150 oC |
291~302 oF |
ASTM D648 |
|
Barcol Hardness |
40~46 |
40~46 |
ASTM D2583 |
*3 Cure condition : 24 hours at room temperature then 2hours at 120oC.
*4 Cure condition for HDT : 24 hours at room temperature then 24 hours at 150oC.
1. If TC-907 is blended with cobalt-salt promoters, shelf life will be shortened. Promoted TC-907 must be used within two weeks.
2. The gel time of TC-907 is affected primarily by catalyst concentration and temperature. The variations of cure characteristics may be caused by the variations of catalyst, humidity, pigment, fillers and other additives. It is recommended that the fabricators check the cure characteristics with a small quantity resin before proceeding for bulk production.
3. TC-907 contains organic solvent (styrene). Keep away from heat, sparks and flames.
4. TC-907 is a potentially reactive chemical. Please store it in dark and keep away from heat and direct sunshine.
5. Containers, not completely emptied must be closed immediately after use.
Standard packing is 200 kg steel drum.
contact me for more details of our products