Offer TM-196 High transparency liquid unsaturated resin From China

Model No.: TM-196

CAS No.: 25608-12-2

Other Names: hand lay up FRP vehicle shell resin

MF: C3H5NO)n

EINECS No.: 208-750-2

Type: Synthetic Resin And Plastics

Brand Name: TIANMA

Model Number: TM-196, TM-196

Appearance: Transparent light yellow liquid

Packaging: metal barrel

Usage: hand lay up FRP vehicle shell resin

Net weight: 220kg

Certificate: Msds

storage period: 90 days .but it's 30 days if add thixotropice accelerator

Storage Condition: Below 25℃ in dark

Keywords: hand lay up FRP vehicle shell resin

Place of Origin: Jiangsu, China

Purity: 66-72

Brand: TIANMA

Product Description

TM—196 general purpose UP resin

TM—196 general purpose IG UP resin features medium viscosity, good tenacity and mechanical strength, suitable for hand lay up FRP vehicle shell ,marine parts and other FRP products, this resin has achieved CCS certificate.

1. liquid resin property:

item	unit	standard	testing method
appearance	——	transparent light yellow liquid	GB/T 8237.4.1.1
viscosity	25℃,Pa.S	0.60~1.20	GB/T 7193.1
gel time	25℃,min	9.1~18.9	GB/T 7193.6
acid value	mgKOH/g	17~25	GB/T 2895
solid content	%	64~70	GB/T 7193.3

gel time: 50% cyclohexanone peroxide paste 4%; curing agent E1: 4%:

2. casting body property(for reference)

Item	Unit	Measured data	Testing method
Barcol hardness	——	46	GB 3854—83
distortion temperature	℃	72	GB 1634—04
bending strength	Mpa	120	GB2570—95
tensile strength	Mpa	76	GB2568—95
elongation	%	2.0	GB2568—95
Impact strength	KJ/M²	13	GB2571—95
Water absorption	%	0.15	GB1462—88

Notes: 1. casting body sample preparation method accord to GB 8237—87.

2. Curing system: curing agent 55% MEKPO: 1%, accelerate E1: 2%.

3. Post cure: 60℃×2h +80℃×2h

3.FRP products property( for reference)

item	unit	measured data	testing method
bending strength	MPa	316	GB/T2570—95
bending modulus	MPa	1.36×10⁴	GB/T2570—95

Notes: 1. FRP sample preparation method accord to GB 8237—87.

2. Curing system: curing agent 55% MEKPO: 2%, accelerate E1: 2%.

4. Post cure: 60℃×3h +110℃×3h

3. Recipe (for reference)

Item	Parts by weight
TM-196 UP resin	100
Curing agent(55%MEKPO 50% cyclohexanone peroxide paste)	2-4
Accelerator E1	1-4(according to local temperature)

4.Storage

Stored under 25℃ shelter,flame and heat isolated, 3 month shelf life.

5. Notes

1. High efficient colorless accelerate is prohibit to choose,will lead to finished product surface sticky phenomenon because of finished product poor curing, fiberglass special accelerate is recommended.

2. If operated in high humidity or high temperature circumstance,finished product surface will also get easily sticky,proper percentage liquefied beeswax is recommended to be added